Product and method for making a three dimensional amorphous metal mass

ABSTRACT

A three dimensional amorphous metal mass suitable for milling is formed wrapping amorphous metal ribbon into a three dimensional shape and then applying adhesive to the three dimensional shape. The adhesive permeates the three dimensional shape. The adhesive is then cured. The three dimensional shape is mechanically contained in three dimensions. If the amorphous metal mass is made as a toroid, then it could be processed into a stator. The stator would then be suitable for use in very high frequency electric motors.

BACKGROUND OF THE INVENTION

[0001] The present invention relates to manufacturing of amorphous metal objects, such as stators.

[0002] Multi-pole rotating electrical devices, such as motors and generators, are comprised of rotors and stators. AC motors rotate by producing a rotating magnetic field pattern in the stator that causes the rotor to follow the rotation of this field pattern. As the frequency varies, the speed of the rotor varies. To increase the speed of the motor, the frequency of the input source must be increased.

[0003] High frequency motors manufactured with the proper materials can be very efficient. For certain applications, like electric or hybrid cars, highly efficient electric motors are desirable.

[0004] The construction of stators for high frequency electric motors is problematic. Iron or steel stators are quite common in electric motors. However, at high frequencies, such as those greater than 400 Hz, iron or steel stators are no longer practical. The high frequency of the AC source increases the core losses of the iron or steel stator, reducing the overall efficiency of the motor. Additionally, at very high frequencies, the stator may become extremely hot and may cause motor failure.

[0005] For construction of stators used in high frequency electric motors, amorphous metal would be ideal. Amorphous metal is easy to magnetize and demagnetize, which means a stator made with amorphous metals would have low power loss, low temperature rise at high frequency, extremely fast magnetization (high permeability) and easy conversion of electrical to mechanical energy. A stator made of such an amorphous metal would generate less core losses and be able to operate at much higher frequencies, resulting in motors of exceptional efficiency and power density.

[0006] Amorphous metals are commercially produced as ribbon. An example of amorphous metal ribbon is Metglas®, manufactured by Honeywell, Inc. Amorphous metal ribbons are very thin and of varying width. Manufacturing components of amorphous metal ribbon requires winding the amorphous material into a shape and then heat processing the shape. Simple three dimensional shapes, such as toroids, can currently be constructed from amorphous metal ribbon.

[0007] However, a stator is not a simple three dimensional shape. The stator has numerous slots for accommodating motor coils milled into a general toroid structure. Manufacturing stators of amorphous metal ribbon presents challenges.

[0008] Attempts to create complex three dimensional configurations from amorphous metal ribbon have heretofore been commercially unsuccessful. Various manufacturing techniques have been attempted by industry such as but not limited to: wire electrical discharge machining, electrochemical creep grinding, conventional electrical discharge machining, cutting, stamping, acid etching and fine blanking. None thus far have proven satisfactory for reasons such as cost-effectiveness, manufacturing repeatability, or process cycle time.

[0009] This inability to fabricate complex three dimensional shapes from amorphous ribbon has been the significant impediment to producing high efficiency axial flux motors and generators.

[0010] A method to produce stators from amorphous ribbon in a cost effective, end use functional, high volume capable method that also provides substantial design flexibility for end use requirements is highly desirable.

SUMMARY OF THE INVENTION

[0011] The aforementioned problems are overcome in the present invention. A method for forming a three dimensional amorphous metal mass suitable for milling consists of wrapping amorphous metal ribbon into a three dimensional shape , then applying adhesive to the three dimensional shape. The adhesive is then cured and the cured form is mechanically constrained in three dimensions. The three dimensional amorphous metal so formed can be milled using a horizontal mill, a vertical mill, a computer numeric control (CNC) machine, or any other common milling equipment. Thus, complex three dimensional amorphous metal shapes can be created.

[0012] The ability to create three dimensional amorphous metal shapes allows the use of amorphous metal for a variety of applications heretofore foreclosed by the mechanical characteristics of amorphous metal ribbon. For example, to manufacture an amorphous metal stator, amorphous metal ribbon is wound into a toroid. The toroid is then placed in a milling assembly. Adhesive is applied to the toroid, and then cured. The toroid is then milled into a stator shape. Thermally processing the stator shape results in a stator. The amorphous metal stator is useful in many applications, especially high frequency electric motors.

[0013] These and other objects, advantages and features of the invention will be more readily understood and appreciated by reference to the detailed description of the drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014]FIG. 1 shows an amorphous metal ribbon being wound on an inner ring;

[0015]FIG. 2 shows an inner containment hat;

[0016]FIG. 3 shows an outer containment hat;

[0017]FIG. 4 shows a milling assembly;

[0018]FIG. 5 shows a milling assembly being milled; and

[0019]FIG. 6 shows an amorphous metal stator.

DETAILED DESCRIPTION OF THE DRAWINGS

[0020]FIG. 1 shows amorphous metal ribbon 10 being wound about a winding axis 11 on an inner ring 14. Winding machine 13 contains amorphous metal ribbon roll 12. Inner ring 14 is placed on winding plate 16. Inner ring 14 can be a solid ring or a thin steel strip. Amorphous metal ribbon 10 is wound on inner ring 14, forming amorphous metal toroid 18. Amorphous metal toroid 18 has an inner side surface 15, an outer side surface 17, a top 19, and a bottom 21.

[0021] While FIG. 1 shows the formation of an amorphous metal toroid 18, it will be appreciated that a three dimensional shape could be created with a geometry distinctly different from the amorphous metal toroid 18. For example, it would be possible by winding around four corners to create a rectangular prism.

[0022] Amorphous metal ribbon 10 can be wound using a variety of machines and methods. Preferably, a consistent, firm toroid will have at least an 85% wind density compared to the inherent ribbon density. Amorphous metal toroid 18 is then removed from winding plate 16. Amorphous metal ribbon 10 can be wound around the inner ring 14 while attached to the inner containment hat 20 as a single unit.

[0023] An adhesive is then applied to the amorphous ribbon toroid 18 in a manner to permeate the amorphous metal toroid 18. Inner ring 14 is still contained within the amorphous ribbon toroid 18. A suitable adhesive is Scotch Cast adhesive by 3M, diluted by acetone so as to achieve about a 20% mix by volume. The adhesive is applied to amorphous ribbon toroid 18 by an ambient atmospheric soak process. Amorphous ribbon toroid 18 is immersed in the adhesive until the adhesive infiltrates the layers.

[0024] Alternatively, the adhesive could be applied by immersing amorphous ribbon toroid 18 into the adhesive inside a vessel that is evacuated of air. The vacuum created would enhance the infiltration of the adhesive into the amorphous ribbon toroid 18 layers. Alternative resins, epoxies or adhesives may be used. Different brands as well as different types of resins, epoxies or adhesives may be used. Heat cured epoxies that require various temperatures as well a two stage epoxies that cure at room temperature would also be suitable.

[0025] After amorphous ribbon toroid 18 is sufficiently infiltrated with adhesive, amorphous ribbon toroid 18 is allowed to drain. Once dry, amorphous ribbon toroid 18 is placed inside an oven for curing. Importantly, the temperature for heat curing the adhesive be a fraction of the temperature for heat processing amorphous metal ribbon 10. A preferable fraction is ½, although fractions of ¼ and ¾ might also be satisfactory.

[0026]FIG. 2 shows inner containment hat 20. Inner containment hat 20 is a cylinder comprised of a number of columns 22 extending upward from the inner containment hat base 24. Fingers 26 extend outward from columns 22 at approximately a right angle. Fingers 26 increase in width as they extend further from the columns 22. Fingers 26 are arranged in a circle, forming an annulus 28. The columns 22 and fingers 26 form a plurality of inner containment hat grooves 29.

[0027] Columns 22 of inner containment hat 20 are placed inside inner ring. The height of columns 22 is approximately equal to the height of the amorphous metal toroid 18. The internal diameter of the amorphous metal toroid 18 is about equal to the outer diameter of the inner ring 14.

[0028] Following the placement of inner containment hat within amorphous metal toroid 18, outer containment hat 30 shown in FIG. 3, is placed around amorphous metal toroid 18. Outer containment hat 30 is cylindrical, with a base 32. Bars 34 extend upward from base 32. At the top of each bar 34 is a lug 36 extending inward. Lug 36 for each bar 34 forms a flange for securing the amorphous metal toroid 18 within outer containment hat 30. Bars 34 and lugs 36 form a plurality of outer containment hat grooves 38.

[0029] Milling assembly 40, shown in FIG. 4, is then formed. Amorphous metal toroid 18, still containing inner ring 14, along with the inner containment hat 20 is placed within outer containment hat 30. Lugs 36 and fingers 26 are aligned. Milling assembly 40 contains the amorphous metal toroid 18 within a toroidal geometry. Alternatively, amorphous metal toroid 18 could be placed within outer containment hat 30 and inner containment hat 20 prior to treatment with the adhesive.

[0030] After application of the adhesive and placement within the mechanical constraints of the inner ring 14, inner containment hat 20, and outer containment hat 30, the amorphous metal toroid 18 has sufficient structural integrity to withstand the stresses of milling.

[0031] Milling plate 44 is placed on the bottom of the amorphous metal toroid 18. Milling plate 44 could be the same as winding plate 16.

[0032] Amorphous metal toroid 18, having been treated with an adhesive, is thus firmly contained within a structure, allowing amorphous metal toroid 18 to be milled and formed in three dimensions. Complex shapes can thus be constructed from the metal ribbon toroid 18, allowing structures such as stators to be made from the amorphous metal toroid 18.

[0033] As illustrated by FIG. 5, milling assembly 40 is placed in mill 50. Mill 50 could be a horizontal mill, a vertical mill, a computer numeric control (CNC machine, or any other type of mill. However, mill 50 should preferably have the axis of rotation of the mill tools 52 perpendicular to the axis of the amorphous metal toroid 18. By having the axis of rotation of the mill tool 52 perpendicular to the axis of the amorphous metal toroid 18, the depth and width of the slots milled into the amorphous metal toroid 18 can be finely controlled.

[0034] Mill 50 cuts slots or other geometries into the amorphous metal toroid 18. Inner ring 14, still contained within amorphous metal toroid 18, acts as a positive mechanical stop for the inside edge of amorphous metal toroid 18. Inner ring 14, in conjunction with the epoxy, does not allow strips of amorphous metal ribbon 10 to separate during machining, thereby producing clean and accurate cuts. It also should be noted that an outer containment ring with the same function of inner ring 14 could be employed to facilitate the milling of slots across the entire diameter of the toroid by not allowing strips of amorphous metal ribbon to separate as the cutter exits the toroid.

[0035] After the amorphous metal toroid 18 is milled into a stator shape, milling assembly 40 is removed from mill 50. Milling assembly 40 is then thermally processed in accordance with the recommendations of the manufacturer of amorphous metal ribbon 10. If the amorphous metal ribbon 10 is Metglas®, thermal processing consists of placing milling assembly 40 into a vacuum furnace at 695 degrees Fahrenheit for a thermal processing cycle that is approximately 4 hours in duration where the milling assembly reaches the desired 695 degrees Fahrenheit for at least sixty minutes.

[0036] Following thermal processing, the milling assembly 40 is disassembled by removing outer containment hat 30, inner containment hat 20, and inner ring 14. A lacquer or varnish is applied to prevent rust and tack the layers for handling purposes.

[0037] Amorphous metal toroid 18 has thus been made into an amorphous metal stator 60, shown in FIG. 6. Amorphous metal stator 60 can hold numerous windings. Since it is made of an amorphous metal, it has significantly enhanced magnetic characteristics, making it ideal for use in high efficiency motors.

[0038] The process described above can be readily used in mass production of amorphous metal stators. Further, the time and cost for manufacturing the stator are sufficiently low to allow mass production of the stator.

[0039] The above description is of the preferred embodiment. Various alterations and changes can be made without departing from the spirit and broader aspects of the invention as defined in the appended claims, which are to be interpreted in accordance with the principles of patent law including the doctrine of equivalents. Any references to claim elements in the singular, for example, using the articles “a,” “an,” “the,” or “said,” is not to be construed as limiting the element to the singular. 

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:
 1. A method for forming a three dimensional amorphous metal mass suitable for milling, comprising the steps of: wrapping an amorphous metal ribbon into a three dimensional shape; applying an adhesive to the three dimensional shape to allow permeation of the adhesive into the three dimensional shape; and curing the adhesive.
 2. The method of claim 1 where the step of applying an adhesive to the three dimensional shape comprises at ambient atmospheric soak process.
 3. The method of claim 1 where the step of applying an adhesive to the three dimensional shape comprises: providing a vessel containing adhesive; immersing the three dimensional shape in the adhesive; and evacuating the vessel.
 4. The method of claim 3 where the step of curing the adhesive comprises the step of heat treating the three dimensional shape.
 5. The method of claim 4 where the amorphous metal ribbon has a thermal processing temperature, and the step of curing the adhesive occurs at a heat curing temperature, and the heat curing temperature is a fraction of the thermal processing temperature.
 6. The method of claim 5 where the fraction is about ½.
 7. The method of claim 5 where the fraction is about ¾.
 8. The method of claim 5 where the fraction is about ¼.
 9. A three-dimensional amorphous metal mass suitable for milling made in accordance with claim
 1. 10. A method for forming an amorphous metal toroid suitable for milling comprising the steps: winding an amorphous metal ribbon into a toroid; applying an adhesive to the toroid; and curing the adhesive.
 11. The method of claim 10 where the step of applying an adhesive to the amorphous metal toroid comprises an ambient atmospheric soak process.
 12. The method of claim 10 where the step of applying an adhesive to the amorphous metal toroid comprises: providing a vessel containing adhesive; immersing the amorphous metal toroid in the adhesive; and evacuating the vessel.
 13. The method of claim 12 where the step of curing the adhesive includes a step of heat curing the toroid.
 14. The method of claim 10 where the amorphous metal ribbon has a thermal processing temperature, and the step of heat curing the toroid occurs at a heat curing temperature, and the heat curing temperature is a fraction of the thermal processing temperature.
 15. The method of claim 14 where the fraction is about ½.
 16. The method of claim 14 where the fraction is about ¾.
 17. The method of claim 14 where the fraction is about ¼.
 18. A method for manufacturing an amorphous metal stator comprising the steps of: winding amorphous metal ribbon into a toroid; containing the toroid within a toroidal geometry; milling the toroid into a stator shape; and thermally processing the stator shape into a stator.
 19. The method of claim 18 where the step of containing the toroid within a toroidal geometry comprises the steps of: applying an adhesive to the toroid; and curing the adhesive.
 20. The method of claim 19 where the step of applying the adhesive to the toroid comprises an atmospheric soak process.
 21. The method of claim 19 where the step of applying the adhesive to the toroid includes the steps of: providing a vessel containing the adhesive; immersing the toroid in the adhesive; and evacuating the vessel.
 22. The method of claim 21 including a step of curing the adhesive.
 23. The method of claim 22 where the step of curing the adhesive at a heat treating curing and the step of thermally processing the stator shape into a stator occurs at a thermal processing temperature, and where the heat curing temperature is a fraction of the heat processing temperature.
 24. The method of claim 23 where the fraction is about ½.
 25. The method of claim 23 where the fraction is about ¾.
 26. The method of claim 23 where the fraction is about ¼.
 27. The method of claim 18 where the toroid has a ribbon winding axis, and the step of milling the toroid into a stator shape comprises milling the toroid primarily in an axis perpendicular to the winding axis.
 28. The method of claim 18 where the toroid has a ribbon winding axis, and the step of milling the toroid into a stator shape consists of milling the toroid exclusively in an axis perpendicular to the ribbon winding axis.
 29. A stator made in accordance with claim
 18. 30. A method for manufacturing an amorphous metal stator comprising the steps of: winding amorphous metal ribbon into a toroid; containing the toroid within a milling assembly; applying an adhesive to the toroid; curing the adhesive; milling the toroid into a stator shape; and thermally processing the stator shape into a stator.
 31. The method of claim 30 including the step of: removing the toroid from the milling assembly.
 32. The method of claim 30 where the toroid has an inner side surface, an outer side surface, a top and a bottom.
 33. The method of claim 32 where the step of containing the toroid within a milling assembly comprises placing an inner ring circumferentially about at least a portion of the inner side surface.
 34. The method of claim 32 where the step of containing the toroid within a milling assembly comprises placing an outer ring circumferentially about at least a portion of the outer side surface.
 35. The method of claim 32 where the step of containing the toroid within a milling assembly comprises placing a hat on at least a portion of the top.
 36. The method of claim 32 where the step of containing the toroid within a milling assembly comprises placing a base on at least a portion of the bottom.
 37. The method of claim 32 where the step of containing the toroid within a milling assembly comprises the steps of: placing an inner ring circumferentially about at least a portion of the inner side surface; placing an outer ring circumferentially about at least a portion of the outer side surface; and placing a hat on at least a portion of the top.
 38. The method of claim 37 where the inner ring is placed about substantially all of the inner side surface.
 39. The method of claim 37 where the outer ring is placed about substantially all of the outer side surface.
 40. The method of claim 37 where the hat is placed about substantially all of the top.
 41. The method of claim 37 where a milling plate is placed about substantially all of the bottom.
 42. The method of claim 37 where the hat and the outer ring are integral.
 43. The method of claim 37 where the hat, outer ring and inner ring are integral.
 44. The method of claim 37 including applying a lacquer to stator.
 45. The method of claim 38 including the step of providing milling grooves within the milling assembly.
 46. The method of claim 30 where the toroid has a ribbon winding axis, and the step of milling the toroid into a toroid shape consists of milling the toroid primarily in an axis perpendicular to the winding axis.
 47. The method of claim 30 where the toroid has a winding axis, and the step of milling the toroid into a toroid shape consists of milling the toroid exclusively in an axis perpendicular to the winding axis.
 48. The method of claim 43 where the toroid has a winding axis, and the step of milling the toroid into a toroid shape consists of milling the toroid primarily in an axis perpendicular to the winding axis.
 49. The method of claim 43 where the hat and outer ring have slots, and the step of milling the toroid into a stator shape includes milling through the slots.
 50. The method of claim 43 where the toroid has a winding axis, and the step of milling the toroid into a stator shape consists of milling the toroid exclusively in an axis perpendicular to the winding axis.
 51. The method of claim 48 where the hat and outer ring have slots, and the step of milling the toroid into a stator shape includes milling through the slots.
 52. An amorphous metal stator made from the process of claim
 30. 53. A method for manufacturing an amorphous metal stator comprising the steps of: winding amorphous metal ribbon about a winding axis into a toroid, the toroid having an inner side, an outer side, a top and a bottom; placing an inner ring on the inner side; placing an inner containment hat on the top and inner side; placing an outer containment hat on the top and outer side; placing a retainer around the outer containment hat; applying adhesive to the toroid; curing the adhesive; milling the toroid into a stator shape; and thermally processing the stator shape into a stator.
 54. The method of claim 53 where the inner containment hat has a plurality of inner containment hat slots and the outer containment hat has a plurality of outer containment hat slots, and the step of milling the toroid into a stator shape comprises milling through the plurality of inner containment hat slots and the plurality of outer containment hat slots.
 55. The method of claim 54 including a step of aligning the plurality of inner containment hat slots and the plurality of outer containment hat slots.
 56. The method of claim 53 where the step of milling the toroid into a stator shape occurs primarily on an axis perpendicular to the winding axis.
 57. The method of claim 53 where the step of milling the toroid into a stator shape occurs exclusively on an axis perpendicular to the winding axis.
 58. A stator made in accordance with the method of claim
 53. 